Merbenit 2K60 is a permanently elastic 2-component adhesive with a very fast strength build-up and very good adhesion properties, especially on synthetics which are difficult to bond.
- Fast strength build-up, handling strength achieved after 30 minutes
- Compatible with paints
- Simple processing
- High elasticity, good mechanical strength
- Corrosion protecting
- Free of solvents, isocyanates and silicones
- Non-corrosive on surfaces
- Vibration absorbing
- Very wide adhesion range
- Very good sealing properties
Shore-A-hardness, DIN 53505 = 48
Modulus elongation at 100%,DIN 53504 S2 = ca. 2.0 N/mm²
Elongation at break, DIN 53504 S2 = ca. 150%
Tensile strength after 1h, DIN 53504 S2 = ca. 1.3 N/mm²
Tensile strength after 7d, DIN 53504 S2 = ca. 3.0 N/mm²
Consistency = slightly thixotropic
Tooling time max. = 4 min.
Density = 1.37 ± 0.05 g/cm³
Volume change, DIN EN ISO 10563 ≤ 8%
Temperature resistance after curing = – 40 °C to + 90 °C
Application temperature = + 5 °C to + 40 °C
Temperature of the substrate = + 5 °C to + 40 °C
Shear strength = ca. 3.0 N/mm²
All measurements were performed under normal conditions (23 °C and 50 % relative
Merbenit 2K60 TDS (.pdf)
Flexible bonding in the areas of metal, apparatus and machine construction, plastics technology, air-conditioning and ventilation systems, car body, wagon, vehicle and container construction. Thanks to fast crosslinking it is possible to bond parts in continous working process. The neutral polymerisation allows a connection without thermal or chemical pre-treatment of the assembly parts. Counterbalancing tolerances.
Suitable materials are metals, powder-coated, varnished, galvanised, anodised, chromed or hot zinc dipped surfaces, various plastics, ceramics, stone, concrete and wood. Due to the large variety of different plastics and compositions as well as materials which are susceptible cracks, preliminary tests are recommended.